信賴性保證與失效分析

泰藝電子在生產流程中進行全面性的品質保證工作,踏實執行每一個檢測過程中的環節與步驟,盡全力達到100%的客戶滿意度。泰藝所屬工廠均導入+/-3σ策略來強化產品品質,各項先進並完備的測試儀器,規劃嚴格的檢驗標準及精準的作業規範下,確保產品功能完整,使用穩定,對品質的堅持,贏得客戶高度信賴與肯定!

 

測試項目 測試條件 所參照的國際標準 儀器圖片
氦漏 Leak rate less than 2*10-8 atm.cc/sec MIL-STD-883 1014 FINE LEAK
粗漏 Leak rate less than 2*10-4 atm.cc/sec MIL-STD-883 1014 GROSS LEAK
冷熱衝擊 -55℃, 125℃; soak time is 10 mins,  with total 200 cycles MIL-STD-883 1010 Condition B Thermal Shock
高溫高濕 85℃/85% RH for 500 hrs JESD22-A101 Damp Heat Test
低溫儲存 -40℃ for 500 hrs IEC 60068-2-1 LOW TEMPERATURE STORAGE TEST
老化 25℃, 85℃, 125℃, test in period of  1, 2, 4, 7, 10, 20, 50, 100 days MIL-STD-883 1005 Condition A or B
MIL-STD-883 1008 Condition B
Aging
耐焊性
(Metal Can)
260 ± 5℃ for 10 ± 1 sec MIL-STD-202 210 Condition B Resistance to Soldering Heat
回流焊
(SMD)
Pre-heating: 150℃ to 200℃, 60~120secs.
Heating: 217℃ , 60~150secs.
Peak: 260±5℃ , 25±5secs. Go through twice.
J-STD-020D IR Reflow
焊錫性 First procedure:
Steam Aging 93℃ +3/-5,
8 ± 0.5hrs.
And then:
Dipping 245±5℃ , 5 ± 0.5sec.
JESD22-B102 Resistance to Soldering Heat
機械衝擊 1500g, half-sine, duration: 0.5ms , each axis for 3 times MIL-STD-883 2002 Condition B MECHANICAL SHOCK
振動 10~2000Hz, 1.52mm, 20g, each axis for 4 hrs MIL-STD-883 2007 Condition A Vibration Test
鹽霧實驗 35 ± 2℃, 5% salt spray for 96 hrs MIL-STD-883H
1009.8 condition C
IEC 60068-2-11
SALT SPRAY TEST
彈跳實驗 40g / 6ms ,each axis for 4000 times. IEC 60068-2-29 Bump Test
掉落實驗 70, 80, 90cm, each height for 3 times on hardboard IEC 60068-2-32 DROP TEST
板彎曲實驗 Deflection: 3mm for 30 sec IEC 60068-2-21 BEND TEST
推力實驗 10N for 10 sec IEC 60068-2-21 Press Test & Push Test
壓力實驗 10N for 10 sec IEC 60068-2-21 Press Test & Push Test
拉力實驗 10N for 10 sec IEC 60068-2-21 Tensile Force